Abstract Palmitoleic acid (C16:1n7, POA), a 16-carbon ω-7 monounsaturated functional fatty acid, has been demonstrated a variety of beneficial properties to human health and a wide range of applications in nutrition, medical and chemical industries. Lipozyme® RM IM (Rhizomucor Miehei lipase), a Sn-1,3 specific lipase, was used to catalyze the hydrolysis of seabuckthorn fruit oil and produce monoglycates rich in palmitoleic acid. The fruit oil of seabuckthorn was used as the research object, the dosage of enzyme taking 10% wt.% oil, the influence of water/oil ratio, pH value and reaction temperature to hydrolysis rate were investigated, and then the response surface methodology was applied for optimizing the process conditions. Further, the relationship between the hydrolysis rate and the content of monoacylglycerol was studied under the optimal hydrolysis conditions. The result indicated that the optimal combined condition is as follows: the reaction temperature is 55°C, the pH is 7, the water-oil quality ratio is 1:1. The hydrolysis rate achieved 79.59% within 12 h in the condition above. Under the optimal conditions, the hydrolysis rate was positively correlated with the content of monoester, and the correlation coefficient was 0.999 within the first 10 h of the reaction. The hydrolysis rate was 66.76% at 10 h, and the content of monoglyceride reached the highest of 61.11%. Hereafter, the hydrolysis of monoglyceride began if the reaction continued. The content of palmitoleic acid increased from 27.11% to 40.84%, and that of linoleic acid increased from 4.51% to 33.34%, so the total amount of the two functional fatty acids reached 74.18%. Enzymatic hydrolysis can be an effective way to improve the function of seabuckthorn fruit oil.

Polyhedral oligomeric silsesquioxane (POSS) was added as a reinforcing agent in waterborne polyurethane (WPU)-based coatings to improve their properties. The morphology, structure, thermal stability as well as mechanical properties of the resulting WPU and WPU/POSS hybrid films were investigated. The good compatibility of POSS in the WPU matrices was demonstrated by transmission electron microscopy. Furthermore, Fourier-transform infrared spectroscopy analysis (FTIR) suggested the successful bonding of POSS and WPU matrices. The thermal stability of WPU/POSS hybrids was improved than that of pure WPU according to thermal gravimetric analysis (TGA). The results also revealed the enhancement of the pencil hardness and abrasion resistance of the hybrid films compared with WPU. However, the pull-off adhesion slightly decreased from Grade 0 to Grade 2.